Polymer degradation
Labels:
#reaction
Polymer degradation is a change in the properties—tensile strength, colour, shape, etc.—of a polymer or polymer-based product under the influence of one or more environmental factors, such as heat, light or chemicals. It is often due to the hydrolysis of the bonds connecting the polymer chain, which in turn leads to a decrease in the molecular mass of the polymer. These changes may be undesirable, such as changes during use, or desirable, as in biodegradation or deliberately lowering the molecular mass of a polymer. Such changes occur primarily because of the effect of these factors on the chemical composition of the polymer. Ozone cracking and UV degradation are specific failure modes for certain polymers.
The degradation of polymers to form smaller molecules may proceed by random scission or specific scission. The degradation of polyethylene occurs by random scission—a random breakage of the linkages (bonds) that hold the atoms of the polymer together. When heated above 450°C it degrades to form a mixture of hydrocarbons. Other polymers—like polyalphamethylstyrene—undergo specific chain scission with breakage occurring only at the ends. They literally unzip or depolymerize to become the constituent monomer.
However, the degradation process can be useful from the viewpoints of understanding the structure of a polymer or recycling/reusing the polymer waste to prevent or reduce environmental pollution. Polylactic acid and polyglycolic acid, for example, are two polymers that are useful for their ability to degrade under aqueous conditions. A copolymer of these polymers is used for biomedical applications, such as hydrolysable stitches that degrade over time after they are applied to a wound. These materials can also be used for plastics that will degrade over time after they are used and will therefore not remain as litter.
The degradation of polymers to form smaller molecules may proceed by random scission or specific scission. The degradation of polyethylene occurs by random scission—a random breakage of the linkages (bonds) that hold the atoms of the polymer together. When heated above 450°C it degrades to form a mixture of hydrocarbons. Other polymers—like polyalphamethylstyrene—undergo specific chain scission with breakage occurring only at the ends. They literally unzip or depolymerize to become the constituent monomer.
However, the degradation process can be useful from the viewpoints of understanding the structure of a polymer or recycling/reusing the polymer waste to prevent or reduce environmental pollution. Polylactic acid and polyglycolic acid, for example, are two polymers that are useful for their ability to degrade under aqueous conditions. A copolymer of these polymers is used for biomedical applications, such as hydrolysable stitches that degrade over time after they are applied to a wound. These materials can also be used for plastics that will degrade over time after they are used and will therefore not remain as litter.